供應(yīng) 比利時索爾維 TECHNYL B 216 BLACK 3N PA66/6 TECHNYL? B 216 BLACK 3NPolyamide 66/6 CopolymerSolvay Engineering Plastics產(chǎn)品說明：TECHNYL? B 216 Black 3N is an unreinforced copolyamide 66/6, medium viscosity, for injection moulding. This grade offers an excellent combination between impact resistance, rigidity, thermal resistance and surface appearance.物性信息：基本信息黃卡編號E特性良好的流動性脫模性能良好優(yōu)良外觀用途工業(yè)應(yīng)用汽車領(lǐng)域的應(yīng)用通用消費品應(yīng)用領(lǐng)域機構(gòu)評級EC 1907/2006 (REACH)RoHS 合規(guī)性RoHS 合規(guī)外觀黑色灰色自然色形式粒子加工方法注射成型樹脂ID (ISO 1043)PA66/6物理性能干燥調(diào)節(jié)后的單位制測試方法密度1.14--g/cm3ISO 1183/A吸水率 (23°C, 24 hr)1.6--%ISO 62機械性能干燥調(diào)節(jié)后的單位制測試方法拉伸模量 (23°C)30001100MPaISO 527-2/1A拉伸應(yīng)力ISO 527-2/1A 屈服, 23°C85.050.0MPaISO 527-2/1A 斷裂, 23°C75.060.0MPaISO 527-2/1A拉伸應(yīng)變ISO 527-2 屈服, 23°C3.625%ISO 527-2 斷裂, 23°C30--%ISO 527-2彎曲模量 (23°C)30001200MPaISO 178彎曲應(yīng)力 (23°C)12550.0MPaISO 178沖擊性能干燥調(diào)節(jié)后的單位制測試方法簡支梁缺口沖擊強度 (23°C)5.016kJ/m2ISO 179/1eA簡支梁無缺口沖擊強度 (23°C)無斷裂--ISO 179/1eU懸壁梁缺口沖擊強度 (23°C)5.016kJ/m2ISO 180熱性能干燥調(diào)節(jié)后的單位制測試方法熱變形溫度 (1.8 MPa, 未退火)67.0--°CISO 75-2/Af熔融溫度242--°CISO 11357-3電氣性能干燥調(diào)節(jié)后的單位制測試方法表面電阻率1.0E+151.0E+14ohmsIEC 60093體積電阻率1.0E+151.0E+15ohms·cmIEC 60093介電強度 (2.00 mm)2624kV/mmIEC 60243-1相對電容率3.003.20IEC 60250耗散因數(shù)0.0300.10IEC 60250漏電起痕指數(shù)IEC 60112 解決方案 A600600VIEC 60112 解決方案 B575--VIEC 60112可燃性干燥調(diào)節(jié)后的單位制測試方法UL 阻燃等級UL 94 1.6 mmHB--UL 94 3.2 mmV-2--UL 94極限氧指數(shù)24--%ISO 4589-2注射干燥單位制干燥溫度80°C建議的最大水分含量0.20%料筒后部溫度250 到 260°C料筒中部溫度255 到 265°C料筒前部溫度265 到 275°C模具溫度60 到 80°C注射說明The material is supplied in airtight bags, ready for use. In case that the virgin material has absorbed moisture, it must be dried with a dehumidified air drying e, dew point mini -20°C. Recommended time 2-4hInjection Advice: For unfilled polyamide, Solvay recommends the use of high alloy steel with a weak chromium content. For example: X38CrMoV5-1 (EN Norm) - 1.2367 /1.2343 (DIN Norm). For Mould Temperature, in the case of parts where the surface roughness is required we can recommend a temperature of 90°C to 120°C with an optimum at 105°C. The processing parameters like processing temperatures are a recommendation and can be adjusted in function of injection machine size, part geometry / design