FGS600F40 NC010 物性表物理性能額定值 (公制)額定值 (英制)測(cè)試方法密度1.11 g/cc0.0401 lb/in31.31 g/cc0.0473 lb/in3ISO 1183吸水率0.40 %@Thickness 2.00 mm0.40 %@Thickness 0.0787 inSim. to ISO 62水分吸收0.200 %@Thickness 2.00 mm0.200 %@Thickness 0.0787 inSim. to ISO 62粘度測(cè)試120 cm3/g120 cm3/gISO 307 1157 1628線性成型收縮率,Flow0.019 cm/cm0.019 in/inISO 294-4 2577線性成型收縮率，橫向0.018 cm/cm0.018 in/inISO 294-4 2577熔體流動(dòng)速率33 g/10 min@Load 2.16 kg, Temperature 250 °C33 g/10 min@Load 4.76 lb, Temperature 482 °FISO 1133機(jī)械性能額定值 (公制)額定值 (英制)測(cè)試方法抗張強(qiáng)度(屈服)58.0 MPa8410 psiISO 527-1/-2伸長(zhǎng)率 (斷裂)30 %30 %Nominal; ISO 527-1/-2屈服伸長(zhǎng)率6.0 %6.0 %ISO 527-1/-2拉伸模量2.60 GPa377 ksiISO 527-1/-2彎曲強(qiáng)度85.0 MPa12300 psiISO 178彎曲模量2.40 GPa348 ksiISO 178懸壁梁缺口沖擊強(qiáng)度4.00 kJ/m21.90 ft-lb/in2ISO 180/1A簡(jiǎn)支梁無(wú)缺口沖擊強(qiáng)度NBNBISO 179/1eUNB@Temperature -30.0 °CNB@Temperature -22.0 °FISO 179/1eU簡(jiǎn)支梁缺口沖擊強(qiáng)度0.400 J/cm21.90 ft-lb/in2ISO 179/1eA0.400 J/cm2@Temperature -30.0 °C1.90 ft-lb/in2@Temperature -22.0 °FISO 179/1eA拉伸蠕變模量(1 hr)2600 MPa@Time 3600 sec377000 psi@Time 1.00 hourISO 899-1拉伸蠕變模量(1000 hr)1800 MPa@Time 3.60e+6 sec261000 psi@Time 1000 hourISO 899-1電氣性能額定值 (公制)額定值 (英制)測(cè)試方法體積電阻率= 1.00e+15 ohm-cm= 1.00e+15 ohm-cmIEC 60093表面電阻1.00e+12 ohm1.00e+12 ohmIEC 60093介電強(qiáng)度26.0 kV/mm660 kV/inIEC 60243-1耗散因數(shù)0.0020@Frequency 100 Hz0.0020@Frequency 100 HzIEC 602500.020@Frequency 1.00e+6 Hz0.020@Frequency 1.00e+6 HzIEC 60250相比耐漏電起痕指數(shù)(CTI)600 V600 VIEC 60112熱性能額定值 (公制)額定值 (英制)測(cè)試方法線形熱膨脹系數(shù) - 流動(dòng)110 μm/m-°C61.1 μin/in-°FISO 11359-1/-2線性熱膨脹系數(shù),橫向流動(dòng)120 μm/m-°C66.7 μin/in-°FISO 11359-1/-2比熱容2.11 J/g-°C0.504 BTU/lb-°F導(dǎo)熱系數(shù)0.210 W/m-K1.46 BTU-in/hr-ft2-°Fof melt熔融溫度225 °C437 °F10°C/min; ISO 11357-1/-3載荷下熱變形溫度(0.46 MPa)115 °C239 °FISO 75-1/-2180 °C356 °Fannealed; ISO 75-1/-2載荷下熱變形溫度(1.8 MPa)50.0 °C122 °FISO 75-1/-260.0 °C140 °Fannealed; ISO 75-1/-2維卡軟化溫度175 °C347 °F50°C/h 50N; ISO 306玻璃化轉(zhuǎn)變溫度，Tg55.0 °C131 °F10°C/min; ISO 11357-1/-2可燃性(UL94)HB@Thickness 1.50 mmHB@Thickness 0.0591 inIEC 60695-11-10HB@Thickness 0.800 mmHB@Thickness 0.0315 inIEC 60695-11-10極限氧指數(shù)22 %22 %ISO 4589-1/-2材料描述測(cè)試方法Delivery FormPellets部件標(biāo)識(shí)代碼PBTISO 11469加工Injection Moulding供貨地區(qū)Asia PacificEuropeGlobalNear East/AfricaNorth AmericaSouth and Central America樹(shù)脂識(shí)別PBT