Acetal (POM) Copolymer
Celanese Corporation
25% 長(cháng)玻璃纖維
產(chǎn)品說(shuō)明：
Material code according to ISO 1043-1: POM
Acetal copolymer reinforced with 25 weight percent long glass fibers. The fibers are chemically coupled to the POM matrix. The pellets are cylindrical and normally as well as the embedded fibers 10 mm long.
Parts molded of CELSTRAN have outstanding mechanical properties such as high strength and stiffness combined with high heat deflection. The notched impact strength is increased at elevated and low temperatures due to the fiber skeleton built in the parts. The long fiber reinforcement reduces creep significantly.
The very isotropic shrinkage in the molded parts minimizes the warpage.
Complex parts can be manufactured with high reproducibility by injection molding.
Application field: Functionial/structural parts for automotive
物性信息：
| 填料/增強材料 | 長(cháng)玻璃纖維, 25% 填料按重量 |
| 特性 | 剛性，高 高強度 共聚物 化學(xué)耦合 抗撞擊性，良好 良好的抗蠕變性 耐低溫沖擊 |
| 用途 | 汽車(chē)領(lǐng)域的應用 |
| RoHS 合規性 | 聯(lián)系制造商 |
| 形式 | 粒子 |
| 加工方法 | 注射成型 |
| 樹(shù)脂ID (ISO 1043) | POM |
| 密度 | 1.59 | g/cm3 | ISO 1183 |
| 拉伸模量 | 10300 | MPa | ISO 527-2/1A/1 |
| 拉伸應力 (斷裂) | 177 | MPa | ISO 527-2/1A/5 |
| 拉伸應變 (斷裂) | 2.4 | % | ISO 527-2/1A/5 |
| 彎曲模量 (23°C) | 9190 | MPa | ISO 178 |
| 彎曲應力 (23°C) | 265 | MPa | ISO 178 |
| 簡(jiǎn)支梁缺口沖擊強度 (23°C) | 35 | kJ/m2 | ISO 179/1eA |
| 干燥溫度 | 80.0 到 90.0 | °C | |
| 干燥時(shí)間 | 3.0 | hr | |
| 建議的最大水分含量 | 0.15 | % | |
| 料筒后部溫度 | 180 到 195 | °C | |
| 料筒中部溫度 | 190 到 200 | °C | |
| 料筒前部溫度 | 195 到 205 | °C | |
| 射嘴溫度 | 195 到 205 | °C | |
| 加工（熔體）溫度 | 195 到 205 | °C | |
| 模具溫度 | 70.0 到 110 | °C | |
| 注塑壓力 | 60.0 到 120 | MPa | |
| 注射速度 | 中等 | ||
| 保壓 | 60.0 到 120 | MPa | |
| 背壓 | 0.00 到 3.00 | MPa |